gold spring bars Vs gold plated spring bars

I noticed that all the solid gold Rolex models I have seen all have gold spring bars or what appears to be gold.

I understand the reason why the gold spring bars are mainly used is that the steel tips would be too hard on the soft gold and therefore gold is used to avoid cutting into the gold cavity as gold is soft.

Until recently, I never expected to find gold plated spring bars as I thought they were all solid gold.I believe gold plated would not serve any purpose other than for cosmetic appearance. My question is; would that small plate of gold really be effective to avoid a steel spring bar putting too much wear on the soft gold? How would one tell which is plated and which is solid apart from trying to scratch them?
timelord is offline   Reply With Quote
Old 29 June 2012, 06:49 PM   #2
Mr. Krabs
Member
 
Join Date: Jun 2012
Location: California
Watch: TT SUB / PVD / YM2
Posts: 77
You can probably weight them and tell which ones are solid gold. Plated will be just as good as the solid gold.
Mr. Krabs is offline   Reply With Quote
Old 24 January 2017, 03:03 AM   #3
Grey.Coupe
"TRF" Member
 
Grey.Coupe's Avatar
 
Join Date: Dec 2009
Location: NC, USA
Posts: 555
Plated steel much harder...
Grey.Coupe is offline   Reply With Quote
Old 24 January 2017, 03:55 AM   #4
T. Ferguson
"TRF" Member
 
T. Ferguson's Avatar
 
Join Date: Oct 2012
Location: Left Coast
Posts: 7,025
I'd be more concerned that solid gold spring bars might bend/twist/torque and fail. If anything I would expect Rolex would put a small stainless steel sleeve into the lug holes to avoid the wear issue you're referring to. Seems to me if wear is a problem then any gold plate would eventually wear off. Though in practice it is doubtful the spring bars actually move or pivot that much.
__________________
Some days it's just not worth chewing through the restraints.
T. Ferguson is offline   Reply With Quote
Old 26 January 2017, 10:38 AM   #5
unreformed66
"TRF" Member
 
Join Date: Jan 2017
Location: United States
Posts: 34
I doubt that the gold plated ones are about lessening wear on the gold case. I'd imagine that it's more about corrosion resistance. But I've been wrong before. I've even got a bunch of solid brass spring bars around here that I got in a load of watch parts years ago. I sawed one in half to see if they were really solid brass. They're too thick for most applications though, I'm not sure what they were made to replace.

Last edited by unreformed66; 26 January 2017 at 10:38 AM.. Reason: typo
unreformed66 is offline   Reply With Quote
Reply


Currently Active Users Viewing This Thread: 1 (0 members and 1 guests)
 

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

Wrist Aficionado

My Watch LLC

WatchesOff5th

DavidSW Watches

Takuya Watches

OCWatches


*Banners Of The Month*
This space is provided to horological resources.





Copyright ©2004-2024, The Rolex Forums. All Rights Reserved.

ROLEXROLEXROLEXROLEXROLEXROLEXROLEXROLEXROLEXROLEXROLEXROLEX

Rolex is a registered trademark of ROLEX USA. The Rolex Forums is not affiliated with ROLEX USA in any way.